| Ciri -ciri | aliran tinggi |
| Permohonan | serat |
Analisis Projec | Indeks Kualiti | Hasil ujian | Kaedah ujian | ||
| Penampilan berbutir Black Granular, PC/KG Warna butiran berbutir dan hitam berbutir, PC/kg Butiran besar dan kecil, g/kg | 0 ＜ 5 ＜ 10 37.0 ± 3.70 | 0 0 0 | SH/T 1541.1-2019 | ||
Cairkan Massflowrate Mass (2.16kg), G/10min | 37.0 ± 3.70 | 37.0 | GB/T 3682.1-2018 | ||
| Indeks isotaktik, %(pecahan massa) | ≥96.5 | 98.1 | GB T 2412-2008 | ||
| Kandungan abu, %(pecahan massa) | ≤0.025 | 0.0115 | GB/T 9345.1-2008 | ||
Sifat tegangan Tekanan hasil tegangan (σy), tegasan tegangan MPA pada pecah (σb), ketegangan nominal tegangan MPA pada pemecahan (εtb), % Modulus keanjalan (ET), MPA | ≥30.0 ≥13.0 ≥300 ≥1100 | 31.8 21.1 594 1335 | GB/T 1040.2-2006 | ||
| Modulus lentur, MPA | ≥1000 | 1318 | GB/T 9341-2008 | ||
| Indeks kuning | ≤0 | -5.4 | HG/T 3862-2006 | ||
Fisheye 0.8mm, PC/1520cm^2 0.4mm, 1 8 pc/1520cm^2 | ≤5 ≤15 | 1 8 | GB/T 6595-1986 | ||
|
|
|
 |  |  |
| Ciri -ciri | aliran tinggi |
| Permohonan | serat |
Analisis Projec | Indeks Kualiti | Hasil ujian | Kaedah ujian | ||
| Penampilan berbutir Black Granular, PC/KG Warna butiran berbutir dan hitam berbutir, PC/kg Butiran besar dan kecil, g/kg | 0 ＜ 5 ＜ 10 37.0 ± 3.70 | 0 0 0 | SH/T 1541.1-2019 | ||
Cairkan Massflowrate Mass (2.16kg), G/10min | 37.0 ± 3.70 | 37.0 | GB/T 3682.1-2018 | ||
| Indeks isotaktik, %(pecahan massa) | ≥96.5 | 98.1 | GB T 2412-2008 | ||
| Kandungan abu, %(pecahan massa) | ≤0.025 | 0.0115 | GB/T 9345.1-2008 | ||
Sifat tegangan Tekanan hasil tegangan (σy), tegasan tegangan MPA pada pecah (σb), ketegangan nominal tegangan MPA pada pemecahan (εtb), % Modulus keanjalan (ET), MPA | ≥30.0 ≥13.0 ≥300 ≥1100 | 31.8 21.1 594 1335 | GB/T 1040.2-2006 | ||
| Modulus lentur, MPA | ≥1000 | 1318 | GB/T 9341-2008 | ||
| Indeks kuning | ≤0 | -5.4 | HG/T 3862-2006 | ||
Fisheye 0.8mm, PC/1520cm^2 0.4mm, 1 8 pc/1520cm^2 | ≤5 ≤15 | 1 8 | GB/T 6595-1986 | ||
|
|
|
| | |