| Vipengee | Uwazi wa juu |
| Maombi | mboga za kila siku |
Bidhaa ya uchambuzi | Sehemu | Lengo la ubora | Matokeo | Kiwango |
Kuonekana | / | Chembe za asili, hakuna uchafu | Chembe za asili, hakuna uchafu | Ukaguzi wa kuona |
Granule nyeusi | PCS /kg | 0 | 0 | SH/T 1541.1-2019 |
Snakeskin granule na granule ya tairi | PCS /kg | Ripoti | 11 | SH/T 1541.1-2019 |
Granule kubwa na ndogo | g/kg | ≤50 | 0.2 | SH/T 1541.1-2019 |
Wiani | g/cm^3 | ≤1 | 0.9 | SH/T 1541.1-2019 |
Kiwango cha mtiririko wa misa (MFR) | g/10min | 35 ~ 42 | 41.7 | GB/T 3682.1-2018 |
Shrinkage ya Molding （SMP) | % | 1.1 | 1.1 | GB/T 9345.1-2008 |
| Index ya manjano | / | ≤0 | -8.2 | HG/T 3862-2006 |
| Mafadhaiko ya mavuno ya tensile | MPA | ≥22.0 | 26.6 | GB/T 1040.2-2022 |
| Modulus ya kubadilika | MPA | ≥850 | 990 | GB/T 9341-2008 |
| Shrinkage ya Molding （SMN) | % | 1.1 | 1.1 | GB/T 1043.1-2008 |
| Nguvu ya athari ya Charpy (23 ℃) | KJ/M^2 | 4 | 4 | GB/T 1043.1-2008 |
| Haze | % | ≤15.0 | 11 | GB/T 2410-2008 |
|
|
|
 |  |  |
| Vipengee | Uwazi wa juu |
| Maombi | mboga za kila siku |
Bidhaa ya uchambuzi | Sehemu | Lengo la ubora | Matokeo | Kiwango |
Kuonekana | / | Chembe za asili, hakuna uchafu | Chembe za asili, hakuna uchafu | Ukaguzi wa kuona |
Granule nyeusi | PCS /kg | 0 | 0 | SH/T 1541.1-2019 |
Snakeskin granule na granule ya tairi | PCS /kg | Ripoti | 11 | SH/T 1541.1-2019 |
Granule kubwa na ndogo | g/kg | ≤50 | 0.2 | SH/T 1541.1-2019 |
Wiani | g/cm^3 | ≤1 | 0.9 | SH/T 1541.1-2019 |
Kiwango cha mtiririko wa misa (MFR) | g/10min | 35 ~ 42 | 41.7 | GB/T 3682.1-2018 |
Shrinkage ya Molding （SMP) | % | 1.1 | 1.1 | GB/T 9345.1-2008 |
| Index ya manjano | / | ≤0 | -8.2 | HG/T 3862-2006 |
| Mafadhaiko ya mavuno ya tensile | MPA | ≥22.0 | 26.6 | GB/T 1040.2-2022 |
| Modulus ya kubadilika | MPA | ≥850 | 990 | GB/T 9341-2008 |
| Shrinkage ya Molding （SMN) | % | 1.1 | 1.1 | GB/T 1043.1-2008 |
| Nguvu ya athari ya Charpy (23 ℃) | KJ/M^2 | 4 | 4 | GB/T 1043.1-2008 |
| Haze | % | ≤15.0 | 11 | GB/T 2410-2008 |
|
|
|
| | |