| Maombi | Chupa za sindano za matibabu, zinazotumika kama ampoules |
Bidhaa ya uchambuzi | Faharisi ya ubora | Matokeo ya mtihani | Njia ya majaribio |
Muonekano wa Granule, Matangazo meusi, na Granule ya rangi, PC/kg |
|
| SH/T 1541.1 |
Haze | ≤10 | 9 | GB/T 2410 |
Kiwango cha mtiririko wa molekuli, g/10min, 190c/2.16kg | 0.24-0.36 | 0.3 | GB/T3682.1-2018 |
Dhiki ya kupunguka ya Tensile, MPA | ≥9.0 | 11.6 |
|
Shina ya kupunguka ya kupunguka,% | ≥350 | 516 | |
Modulus ya kuinama, MPA | ≥220 | 317 | GB/T 9341 |
Joto la laini la vica, c, Kiwango cha kupokanzwa 50 ℃/h | ≥95 | 100 | GB/T 1533-2000 |
Uzani, g/cm^3 | 0.923-0.929 | 0.925 | GB/T 1033.2 |
|
|
|  |
 |  |  |
| Maombi | Chupa za sindano za matibabu, zinazotumika kama ampoules |
Bidhaa ya uchambuzi | Faharisi ya ubora | Matokeo ya mtihani | Njia ya majaribio |
Muonekano wa Granule, Matangazo meusi, na Granule ya rangi, PC/kg |
|
| SH/T 1541.1 |
Haze | ≤10 | 9 | GB/T 2410 |
Kiwango cha mtiririko wa molekuli, g/10min, 190c/2.16kg | 0.24-0.36 | 0.3 | GB/T3682.1-2018 |
Dhiki ya kupunguka ya Tensile, MPA | ≥9.0 | 11.6 |
|
Shina ya kupunguka ya kupunguka,% | ≥350 | 516 | |
Modulus ya kuinama, MPA | ≥220 | 317 | GB/T 9341 |
Joto la laini la vica, c, Kiwango cha kupokanzwa 50 ℃/h | ≥95 | 100 | GB/T 1533-2000 |
Uzani, g/cm^3 | 0.923-0.929 | 0.925 | GB/T 1033.2 |
|
|
| |
| | |
≤5